Aluminium
EN-AW 1050
Al 99,5
Chemical Composition
|
Fe |
Si |
Zn |
Ti |
Mg |
Mn |
Cu |
Al |
|
0,4 |
0,25 |
0,07 |
0,05 |
0,05 |
0,05 |
0,05 |
99,5 |
Mechanical Properties
|
Temper |
Yield Strength
( MPa ) min-max |
Tensile Strength
( MPa ) min-max |
Elongation (%50)
Min - max |
Hardness
( HB ) min-max
|
|
O/H 111 |
20-35 |
65-80 |
38 |
20-21 |
|
HX2 |
60-85 |
90-100 |
- |
30 |
|
HX4 |
90-105 |
110-115 |
9 |
35-36 |
|
HX6 |
120 |
0 - 130 |
- |
39 |
|
HX8 |
110-140 |
130-150 |
5 |
43 |
|
HX9 |
130-170 |
100-180 |
3 |
48-51 |
Properties and
Applications
High resistance to atmospheric corrosion, very good forming ability, high electric and heat
conductivity, high welding ability, low mechanic properties. Applications such as packing
industry, chemical and nutrient industry, radiator pipes, architect applications, roof coating
and isolations.
Back to Top
5
EN-AW 2007
AlCu4PbMg
Chemical Composition
|
Fe |
Si |
Zn |
Ti |
Mg |
Mn |
Cu |
Pb |
Other |
Al |
|
0,8 |
0,8 |
0,8 |
0,2 |
0,4 - 1,8 |
0,5 – 1,0 |
3,3 – 4,6 |
0,8 -1,5 |
0,3 |
Remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
T3 |
360 |
460 |
- |
115 |
|
T4 |
295 |
445 |
14 |
- |
Properties and
Applications
High fatigue resistance, Heat treatable in high hardness, not suitable for atmospheric
condition, advice on hard coatings and other protective methods. Different machine parts,
screw, pin bolts, defense industry, automotive industry.
Back to Top
5
EN-AW 2011
AlCu6BiBp
Chemical Composition
|
Fe |
Si |
Cu |
Pb |
Bi |
Other |
Al |
|
0,5 |
0,3 |
5,0 – 6,0 |
0,2 – 0,6 |
0,2 – 0,6 |
0,15 |
Remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
T3 |
260- 290 |
310 - 365 |
10 - 15 |
7 - 95 |
|
T4 |
270 |
320 - 350 |
18 |
90 |
|
T6 |
230 - 300 |
310 - 395 |
10 - 12 |
110 |
|
T8 |
275 - 315 |
370 - 420 |
10 - 12 |
115 |
Properties and
Applications
High fatigue resistance, suitable for free machine parts. Low wear resistance for external
mediums, recomended with hard coatings and other protection methods. All kinds of
machine parts, screw, bolt production and for defense industry, automotive industry.
Back to Top
5
EN-AW 2014
AlCu4SiMg
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Ti + Zr |
Other |
Al |
|
0,7 |
0,5 – 1,2 |
3,5 – 5,0 |
0,4 – 1,3 |
0,2 – 0,8 |
0,2 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0 |
85 |
7 - 190 |
7 - 18 |
55 |
|
T4 |
250 - 275 |
400 - 430 |
7 - 18 |
105 - 110 |
|
T6 |
400 - 425 |
450 - 485 |
12 |
135 - 140 |
Properties and
Applications
Suitable for machine production, high machinability, high fatigue strength, increasing
corrosion capacity with coating. Aircraft industry, military vehicle and bridge construction,
weapon production, truck, machine parts, hydraulic and automotive industry.
Back to Top
5
EN-AW 2017A
AlCu4MgSi (A)
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Zn |
Cr |
Zr+Ti |
Other |
Al |
|
0,7 |
0,2 – 0,8 |
3,5 – 4,5 |
0,4 – 1,0 |
0,4 – 1,0 |
0,25 |
0,1 |
0,25 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0 |
70 |
180 |
- |
45 - 50 |
|
T4 |
230 - 275 |
380 - 425 |
- |
95 - 105 |
Properties and
Applications
High mechanic strength, high fatigue strength, corrosion strength increase with coating.
Structural materials which need high strength values, aircraft industry, machine construction,
military parts and automotive industry.
Back to Top
5
EN-AW 2024
AlCu4Mg1
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Cr |
Zn |
Other |
Zi+Ti |
Al |
|
0,5 |
0,5 |
3,8 – 4,9 |
0,3 – 0,9 |
1,2 – 1,8 |
0,1 |
0,25 |
remaining |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0 |
75 |
185 |
20 |
55 |
|
T3 |
340 |
475 |
18 |
120 |
|
T4 |
315 - 330 |
440 - 465 |
20 |
120 |
|
T8 |
450 |
485 |
6 |
130 |
Properties and
Applications
High fatigue strength, corrosion strength increase with coating. Aircraft industry, machine
parts which need high strength values, military parts, defense industry , structural materials
and automotive industry.
Back to Top
5
EN-AW 3003
AlMn1Cu
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Zn |
Other |
Al |
|
0,5 |
0,6 |
0,05 – 0,2 |
1,0 – 1,5 |
0,1 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0/H111 |
35-50 |
100-110 |
25 |
30 |
|
HX2 |
90-120 |
125-140 |
11 |
40 |
|
HX4 |
125-145 |
145-160 |
9 |
45 |
|
HX6 |
150-165 |
170-180 |
6 |
50 |
|
HX8 |
170-185 |
190-205 |
6 |
55 |
|
HX9 |
215 |
245 |
3 |
65 |
Properties and
Applications
Resistant to atmospheric conditions, high welding ability, high tensile and Rolling properties.
Construction industry, nutrient industry for storage tanks, heat exchangers, buharlastýrýcýlar,
and furnace coatings.
Back to Top
5
EN-AW 5005
Al Mg1
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Zn |
Cr |
Other |
Al |
|
0,45 |
0,3 |
0,05 |
0,15 |
0,7-1,1 |
0,2 |
0,1 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0/H111 |
35-45 |
105-120 |
|
32 |
|
HX2 |
80-125 |
125-145 |
13 |
42-45 |
|
HX4 |
110-145 |
145-165 |
11 |
47-50 |
|
HX6 |
130-165 |
165-185 |
8 |
52-55 |
|
HX8 |
160-185 |
190-205 |
7 |
57-60 |
|
HX9 |
1990-210 |
210-225 |
4 |
60-65 |
Properties and
Applications
Heating and cooling equipments, roof coatings, panels, traffic lights, architectural
applications, chemistry industry.
Back to Top
5
EN-AW 5052
Al Mg2,5
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Zn |
Cr |
Other |
Al |
|
0,4 |
0,25 |
0,1 |
0,1 |
2,2-2,8 |
0,1 |
0,15-0,35 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0/H111 |
60-90 |
170-195 |
22 |
50 |
|
HX2 |
130-175 |
210-225 |
14 |
65 |
|
HX4 |
150-200 |
230-250 |
12 |
70-73 |
|
HX6 |
180-225 |
250-270 |
9 |
75-80 |
|
HX8 |
210-250 |
270-290 |
8 |
80-85 |
|
HX9 |
280 |
310 |
4 |
90 |
Properties and
Applications
Higher corrosion resistance, very good welding ability. Boiling bowls, panels, traffic lights,
petrol tanks and its storages, automotive industry.
Back to Top
5
EN-AW 5083
Al Mg 4,5,5Mn 0,7
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Zn |
Cr |
Ti |
Other |
Al |
|
0,4 |
0,4 |
0,1 |
0,4-1,0 |
4,0-4,9 |
0,25 |
0,05-0,25 |
0,15 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0/H111 |
125-145 |
275-300 |
22 |
70-75 |
|
HX2 |
205-240 |
310-330 |
16 |
85-90 |
|
HX4 |
270-275 |
340-360 |
14 |
100 |
|
HX6 |
305 |
380 |
9 |
105 |
|
HX8 |
335 |
400 |
8 |
110 |
|
HX9 |
370 |
420 |
0-5 |
115 |
Properties and
Applications
High welding ability, very good corrosion resistance against salty water, beter cold forming,
extrusion of thin and complex materails are hard. Pressure tanks for ship construction,
welded pieces, pole, platform, storage tanks, pipe, chemical equipments, automotive
industry, mould sector.
Back to Top
5
EN-AW 5086
Al Mg 4
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Zn |
Cr |
Ti |
Other |
Al |
|
0,5 |
0,4 |
0,1 |
0,2-0,7 |
3,5-4,5 |
0,25 |
0,05-0,25 |
0,15 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0/H111 |
100-130 |
240-275 |
23 |
65 |
|
HX2 |
190-220 |
275-305 |
15 |
80-85 |
|
HX4 |
230-250 |
300-330 |
13 |
90-95 |
|
HX6 |
280 |
345 |
9 |
100 |
|
HX8 |
305 |
360 |
8 |
105 |
|
HX9 |
335 |
380 |
0-5 |
110 |
Properties and
Applications
Very good welding ability, very good resistance to salty water, high machinability, high
fatigue resistance. Welded pieces for ship construction, pole, platform, storage tanks, pipe,
chemical equipments.
Back to Top
5
EN-AW 5754
Al Mg 3
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Zn |
Cr |
Ti |
Other |
Al |
|
0,4 |
0,4 |
0,1 |
0,5 |
2,6-3,6 |
0,2 |
0,3 |
0,15 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0/H111 |
80-100 |
190-215 |
24 |
50-55 |
|
HX2 |
130-185 |
220-245 |
14 |
65-70 |
|
HX4 |
160-215 |
240-270 |
12 |
73-75 |
|
HX6 |
190-245 |
265-290 |
9 |
80 |
|
HX8 |
250-270 |
290-315 |
8 |
85-90 |
|
HX9 |
300 |
340 |
0-4 |
95 |
Properties and
Applications
Very high corrosion resistance, very good welding ability, very good fatigue resistance.
Nuclear applications, ship and boat construction, machine parts, pressure moulds, vehicle
bodies, tanker and strongbox manufacturing.
Back to Top
5
EN-AW 6013
Chemical Composition
|
Fe |
Si |
Cr |
Mn |
Mg |
Zn |
Cu |
Ti |
Other |
Al |
|
0,5 |
0,6-1,0 |
0,1 |
0,2-0,8 |
0,8-1,2 |
0,25 |
0,6-1,1 |
0,1 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0 |
|
|
|
|
|
T8 |
379 |
392 |
7 |
MAX130 |
|
T651 |
359 |
379 |
5 |
MAX130 |
Properties and
Applications
High hardness, high corrosion resistance, good welding ability. Aircraft industry, armchair
and door manufacturing, whenever hardness and machinability needed.
Back to Top
5
EN-AW 6060
Al Mg Si
Chemical Composition
|
Fe |
Si |
Cr |
Mn |
Mg |
Zn |
Cu |
Ti |
Other |
Al |
|
0,5 |
0,6-1,0 |
0,1 |
0,2-0,8 |
0,8-1,2 |
0,25 |
0,6-11 |
0,1 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0 |
50 |
100 |
26 |
25 |
|
T8 |
90 |
150 |
26 |
45 |
|
T651 |
65-90 |
130-160 |
20 |
45 |
|
|
185 |
220 |
13 |
50 |
|
|
195-215 |
245 |
12 |
75-85 |
Properties and
Applications
High hardness, high corrosion resistance, good welding ability. Truck and tram floors,
heating and cooling pipes, illumination, stairs, railing, door, window, interior installation,
roof systems.
Back to Top
5
EN-AW 6061
Al Mg 1 SiCu
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Zn |
Cr |
Zr |
Other |
Al |
|
0,7 |
0,4-0,8 |
0,15-0,4 |
0,15 |
0,8-1,2 |
0,25 |
0,04-0,35 |
0,04-035 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0 |
55 |
125 |
26 |
40-30 |
|
T4 |
110-140 |
180-235 |
16-21 |
65 |
|
T6 |
240-270 |
260-310 |
8-12 |
90-95 |
Properties and
Applications
High corrosion resistance, very good welding ability, gains very good cold forming
properties with T4 heat treatment. Train roads heavy work pieces, truck spoilers, aircraft
construction, space ships, sea motors, defense industry, ship manufacturing, helicopter
sides.
Back to Top
5
EN-AW 6063
Al Mg 0,7Si
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Zn |
Cr |
Zr |
Other |
Al |
|
0,35 |
0,2-0,6 |
0,1 |
0,1 |
0,45-0,9 |
0,1 |
0,1 |
0,1 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0 |
50 |
100 |
26 |
25 |
|
T1 |
90 |
150 |
24 |
45 |
|
T4 |
90 |
160 |
21 |
50 |
|
T5 |
110-175 |
150-215 |
12 |
60 |
|
T6
|
170-210
|
205-245
|
12
|
75
|
|
T8 |
240 |
260 |
9 |
80 |
Properties and
Applications
High corrosion resistance, very good welding ability, gains very good cold forming
properties with T4 heat treatment. Electronic parts, electromotor boxes, radiator and other
heat exchangers, pneumatic installation, irrigation pipes, rails, furniture equipments.
Back to Top
5
EN-AW 6082
Al Si 1 MgMn
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Zn |
Cr |
Other |
Al |
|
0,5 |
0,7-1,3 |
0,1 |
0,4-1,0 |
0,6-1,2 |
0,2 |
0,15 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0 |
60 |
130 |
26 |
35 |
|
T1 |
70 |
260 |
24 |
70 |
|
T4 |
170 |
260 |
19 |
70 |
|
T5 |
250-275 |
290-325 |
19 |
70 |
|
T6 |
260-310 |
310-340 |
19 |
95 |
Properties and
Applications
High corrosion resistance, very good welding ability, gains very good cold forming
properties and stabilization after T4 heat treatment, not very suitable for complex parts.Heavy rail road work pieces, sea boat, truck spoilers, bicycle manufacturing, machine
industry.
Back to Top
5
EN-AW 7020
Al Zn4,5 Mg1
Chemical Composition
|
Fe |
Si |
Cu |
Mn |
Mg |
Zn |
Cr |
Zi+Ti |
Other |
Al |
|
0,4 |
0,35 |
0,2 |
0,05-0,5 |
1,0-1,4 |
4,0-5,0 |
0,1-0,35 |
0,08-0,25 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0 |
80 |
180 |
|
45-55 |
|
T5 |
290-315 |
350-375 |
8-14 |
10 |
|
T6 |
290-315 |
350-380 |
8-12 |
105-125 |
Properties and Applications
Highly fatigue resistance, highly welding ability resistance, not appropriate for cold bending,
necessary precautions should be taken against tension. Welded engineering structural
materials, railway car’s bodies, truck pieces, electric poles, container production.
Back to Top
5
EN-AW 7075
Al Zn5 ,5MgCu
Kimyasal
Kompozisyon
|
Fe |
Si |
Cu |
Mn |
Mg |
Zn |
Cr |
Zi+Ti |
Other |
Al |
|
0,5 |
0,5 |
1,2-2,0 |
0,3 |
2,1-2,9 |
5,1-6,1 |
0,18-0,28 |
0,25 |
0,15 |
remaining |
Mechanical
Properties
|
Temper |
Yield
Strength
( MPa ) min-max |
Tensile
Strength
( MPa ) min-max |
Elongation (% 50 )
Min - max |
Hardness
( HB ) min-max
|
|
0 |
105 |
225 |
17 |
60 |
|
T6 |
460-505 |
530-570 |
10 |
150-150 |
|
T7 |
435 |
505 |
12 |
140 |
Properties
and Applications
High fatigue resistance, recomended that usage with a protective in external surroundings.
Defense industry, high tension structural materials in aircraft industry, mould
manufacturing, nuclear applications, whenever high strength and machinability needed.
Back to Top
5
|