Aluminium Bronzes
| |
|
|
| |
|
|
| |
DIN |
|
|
|
Alloy |
CuAl9Ni |
|
|
| |
NiAlBz-F50 |
|
|
|
Standart |
DIN 1714 |
|
|
|
Alloy Number |
2.0970 |
|
|
| |
|
|
|
|
Chemical Composition |
|
Mechanical Properties |
| |
|
|
|
Cu |
82,0 min. |
|
|
DIN |
|
|
Al |
8,5 - 10,0 |
|
Rm |
≥ 530 |
|
|
Ni |
1,5 - 4,0 |
|
Rp 0,2 |
≥ 230 |
|
|
Fe |
1,0 - 3,0 |
|
A5 |
≥ 20 |
|
|
Mn |
2,5 max. |
|
HB |
≥ 120 |
|
| |
|
|
|
|
kg/dm3 |
ca. 7,5 |
|
|
Back to Top
5
| |
|
|
| |
|
|
| |
DIN |
|
|
|
Alloy |
CuAl10Ni |
|
|
| |
NiAlBz-F60 |
|
|
|
Standart |
DIN 1714 |
|
|
|
Alloy Number |
2.0975 |
|
|
| |
|
|
|
|
Chemical Composition |
|
Mechanical Properties |
| |
|
|
|
Cu |
76,0 min. |
|
|
DIN |
|
|
Al |
8,5 - 11,0 |
|
Rm |
≥ 700 |
|
|
Ni |
4,0 - 6,5 |
|
Rp 0,2 |
≥ 300 |
|
|
Fe |
3,5 - 5,5 |
|
A5 |
≥ 13 |
|
|
Mn |
3,0 max. |
|
HB |
≥ 160 |
|
| |
|
|
|
|
kg/dm3 |
ca. 7,6 |
|
|
|
Özellikler ve Kullanım
Yerleri |
Guide valves , corrosion resistance and parts which are
contact with salty water, propeller, wear resistance ring,
gears. |
Back to Top
5
| |
|
|
| |
|
|
| |
DIN |
|
|
|
Alloy |
CuAl11Ni |
|
|
| |
NiAlBz-F68 |
|
|
|
Standart |
DIN 1714 |
|
|
|
Alloy Number |
2.0980 |
|
|
| |
|
|
|
|
Chemical Composition |
|
Mechanical Properties |
| |
|
|
|
Cu |
73,0 min. |
|
|
DIN |
|
|
Al |
9,0 - 12,3 |
|
Rm |
≥ 750 |
|
|
Ni |
5,0 - 7,5 |
|
Rp 0,2 |
≥ 400 |
|
|
Fe |
4,0 - 7,0 |
|
A5 |
≥ 5 |
|
|
Mn |
2,5 max. |
|
HB |
≥ 185 |
|
| |
|
|
|
|
kg/dm3 |
ca. 7,6 |
|
|
Back to Top
5
| |
|
|
| |
|
|
| |
DIN |
|
|
|
Alloy |
CuAl10Fe |
|
|
| |
FeAlBz-F50 |
|
|
|
Standart |
DIN 1714 |
|
|
|
Alloy Number |
2.0940 |
|
|
| |
|
|
|
|
Chemical Composition |
|
Mechanical Properties |
| |
|
|
|
Cu |
83,0 min. |
|
DIN |
|
|
Al |
8,0 - 11,0 |
|
Rm |
≥ 550 |
|
Ni |
3,0 max. |
|
Rp 0,2 |
≥ 200 |
|
Fe |
2,0 - 4,0 |
|
A5 |
≥ 15 |
|
Mn |
1,0 max. |
|
HB |
≥ 115 |
| |
|
|
|
|
kg/dm3 |
ca. 7,5 |
|
|
|
Properties and Applications |
Wear and salty water resistance which has wide place in,
ship construction, chemical and nutrient industry. Linings,
rings, helix gears, wear plates, valves linings, pick up
grapples, construction of acid resistance armatures and
hydraulic parts |
Back to Top
5
| |
|
|
| |
|
|
| |
DIN |
|
|
|
Alloy |
CuAl10Ni5Fe4 |
|
|
|
Standart |
DIN 17665, 17672 |
|
|
|
Alloy Number |
2.0966 |
|
|
| |
|
|
|
|
Chemical Composition |
|
Mechanical Properties |
| |
|
|
|
Cu |
rest |
|
DIN |
|
|
Al |
8,5 - 11,0 |
|
Rm |
≥ 640 |
|
Ni |
4,0 - 6,0 |
|
Rp 0,2 |
≥ 270 |
|
Fe |
2,0 - 5,0 |
|
A5 |
≥ 15 |
|
Mn |
1,5 max. |
|
HB |
≥ 180 |
| |
|
|
|
|
kg/dm3 |
ca. 7,5 |
|
|
|
Properties and Applications |
Good corrosion resistance, wear resistance rings and
couch parts. |
Back to Top
5
| |
|
|
| |
|
|
| |
DIN |
|
|
|
Alloy |
CuAl10Fe3Mn2 |
|
|
|
Standart |
DIN 17665, 17672 |
|
|
|
Alloy Number |
2.0936 |
|
|
| |
|
|
|
|
Chemical Composition |
|
Mechanical Properties |
| |
|
|
|
Cu |
rest |
|
DIN |
|
|
Al |
8,5 - 11,0 |
|
Rm |
≥ 590 |
|
Ni |
2,0 - 4,0 |
|
Rp 0,2 |
≥ 250 |
|
Fe |
1,5 - 3,5 |
|
A5 |
≥ 12 |
|
Mn |
1,0 max.. |
|
HB |
≥ 150 |
| |
|
|
|
|
kg/dm3 |
ca. 7,6 |
|
|
|
Properties and Applications |
High temperature resistance parts, corrosion resistance
linings, rings, wear plates |
Back to Top
5
| |
|
|
| |
|
|
| |
DIN |
|
|
|
Alloy |
CuAl11Ni6Fe5 |
|
|
|
Standart |
DIN 17665, 17672 |
|
|
|
Alloy Number |
2.0978 |
|
|
| |
|
|
|
|
Chemical Composition |
|
Mechanical Properties |
| |
|
|
|
Cu |
rest |
|
|
DIN |
|
|
Al |
10,5 - 12,5 |
|
Rm |
≥ 590 |
|
|
Ni |
5,0 - 7,5 |
|
Rp 0,2 |
≥ 250 |
|
|
Fe |
4,8 - 7,3 |
|
A5 |
≥ 12 |
|
|
Mn |
1,5 max.. |
|
HB |
≥ 150 |
|
| |
|
|
|
|
kg/dm3 |
ca. 7,4 |
|
|
|
Properties and Applications |
Can be mixed with CuAl10Ni5Fe4,but it has higher
mechanic values. Heavy bearings and machine parts |
Back to Top